Pengaruh Penambahan Additive Gas Block Pada Variasi Temperatur Terhadap Kualitas Bubur Semen Plug Di Laboratorium Cementing Pt. Elnusa Tbk.


Oleh : Giri Mulyadi

Info Katalog

Nomor Panggil : 648/TP/2017

Penerbit : FTKE - Usakti

Kota Terbit : Jakarta

Tahun Terbit : 2017

Pembimbing 1 : Bayu Satyawira

Pembimbing 2 : Widia Yanti

Subyek : Drilling techniques;Cement - Hardening process

Kata Kunci : hardening process, cement slurry, gas block


File Repositori
No. Nama File Ukuran (KB) Status
1. 2017_TA_TM_07110314_Halaman-judul.pdf 935.98
2. 2017_TA_TM_07110314_Bab-1.pdf 91.32
3. 2017_TA_TM_07110314_Bab-2.pdf 744.92
4. 2017_TA_TM_07110314_Bab-3.pdf 9610.39
5. 2017_TA_TM_07110314_Bab-4.pdf 158.2
6. 2017_TA_TM_07110314_Bab-5.pdf 81.09
7. 2017_TA_TM_07110314_Bab-6.pdf 70.85
8. 2017_TA_TM_07110314_Daftar-pustaka.pdf 91.68

P Proses pengerasan semen terbagi menjadi beberapa fase, dimulai dari faseliquid hingga fase solid. Pada masa peralihan antara fase liquid hingga solid,terdapat proses dimana pengerasan bubur semen akan memasuki fase semi-solid,dimana liquid akan membentuk sebuah gel. Fase ini kerap membuat gas masuk kedalam matriks semen yang biasa disebut gas migration. Untuk mencegah haltersebut, campuran bubur semen dengan zat aditif diperlukan untuk mengisimatriks batuan dengan baik. Gas block adalah zat aditif yang dapat mengisimatriks batuan. Ukuran partikelnya yang sangat kecil membuat gas block sebagaiaditif yang tepat karena terbuat dari micro silica.Penelitian ini dilakukan untuk mengetahui pengaruh penambahan zat aditif“Gas Block” pada variasi temperatur BHCT (150°F, 175°F, dan 200°F) terhadaprheology, free water, fluid loss, thickening time, dan compressive strength bubursemen. Tes laboratorium dilakukan dengan bahan semen kelas G, air mineral.Program penelitian yang digunakan adalah penyemenan plug, kedalaman 6562 ft,dan densitas 15,8 ppg.Dari hasil penelitian, diperoleh kesimpulan bahwa penambahan aditif gasblock berfungsi sebagai bahan akselerasi thickening time, dengan pengaruh lainyang dapat meningkatkan nilai early compressive strength, menurunkan nilai fluidloss, serta memberikan pengaruh signifikan pada nilai rheology dan free water.Kenaikan temperatur mempercepat thickening time semen, mempercepatpembentukan strength awal semen dan hasil akhir compressive strength.

C Cement hardening process is divided into several phases, starting fromliquid phase to solid phase. In the transitional period between the liquid to thesolid phase, there is a process, in which the hardening of cement slurry will enterthe semi-solid phase wherein the liquid will form a gel. This phase often makesthe gas fit into the cement matrix, commonly called gas migration. A mixture ofcement slurry with additives is needed to prevent gas migration. Gas blocks areadditives that can fill the rock matrix. The extremely small size particles make thegas block right additive as it is made of micro silica.This study was conducted to determine the effect of the addition of gasblock additive on temperature variation BHCT (150°F, 175°F, and 200°F)towards rheology, free water, fluid loss, thickening time, and compressivestrength of cement slurry. Laboratory test was conducted using class G cementand mineral water. Plug cementing, a depth of 6562 ft, and density 15.8 ppg wereused by this research program.Based on the research, it is resulted that addition of gas block additiveserves as acceleration material within the thickening time. Meanwhile, otherinfluences could also increase the value of early compressive strength, reducefluid loss, and provide significant impact towards rheology and free water.Temperature rise accelerates the thickening time of cement, the formation of earlystrength cement, and the final compressive strength.