Studi Laboratorium Pengaruh Penggunaan Pasir Kuarsa Sebagai Aditif Terhadap Sifat Fisik Semen Kelas G Sesuai Standar Api 10a


Oleh : Aditya Pramudita

Info Katalog

Nomor Panggil : 622/TP/2017

Penerbit : FTKE - Usakti

Kota Terbit : Jakarta

Tahun Terbit : 2017

Pembimbing 1 : Bayu Satyawira

Pembimbing 2 : Cahaya R.

Subyek : Cement - Compressive strength;Cementing - Drilling operation

Kata Kunci : cementing, additive, cement base


File Repositori
No. Nama File Ukuran (KB) Status
1. 2017_TA_TM_07111008_Halaman-judul.pdf 2868.12
2. 2017_TA_TM_07111008_Bab-1.pdf 17.54
3. 2017_TA_TM_07111008_Bab-2.pdf 209.48
4. 2017_TA_TM_07111008_Bab-3.pdf 463.35
5. 2017_TA_TM_07111008_Bab-4.pdf 84.8
6. 2017_TA_TM_07111008_Bab-5.pdf 28.09
7. 2017_TA_TM_07111008_Bab-6.pdf 17.35
8. 2017_TA_TM_07111008_Halaman-judul.pdf 2868.12
9. 2017_TA_TM_07111008_Lampiran.pdf 1019.91

S Salah satu faktor yang mempengaruhi kualitas konstruksi sumur adalahsejauh mana kualitas semen yang digunakan. Agar hasil penyemenan sesuai denganyang diinginkan, sifat – sifat bubur semen harus sesuai dengan kondisi formasi.Kualitas bubur semen yang akan digunakan dalam proses penyemenan dapat dilihatdari berbagai parameter kualitas semen, meliputi nilai compressive strength yangcukup besar dan thickening time yang sesuai target penyemenan.Tujuan dari penelitian ini adalah untuk mengetahui seberapa besarpeningkatan compressive strength dan thickening time yang terjadi pada sampelsemen yang telah ditambahkan additive Pasir Kuarsa bila dibandingkan dengansemen dasar.Hasilnya adalah menjadikan additive Pasir Kuarsa sebagai salah satualternatif additive yang dapat dipertimbangkan dalam hal peningkatan strengthsemen pemboran pada sumur dengan kondisi temperatur dan tekanan yang tinggi.Hasil test yang didapat dengan kandungan air 44% dan 50% Pengujian additiveuntuk nilai compressive strength sangat efektif pada kandungan air 44% dengantemperatur 27C dan 80C hasil test yang didapat sebesar 2161 psi dan 5087 psi.Sedangkan pada air 50% terjadi penurunan compressive strength dan thickeningtime-nya, dengan konsentrasi aditif 7% nilai compressive strength tertinggi sebesar4148 psi pada temperatur 80ºC.

O One of the factor that affect the quality of well construction is the quality ofcement used. In order for the cementing accordance with the desired, properties ofcement slurry must compatible with the condition of formation. The quality ofcement slurry to be used in process of cementing could be observed from severalparameter, include the large value of compressive strength and thickening timebased on target cementing.The purpose of this study is to find how much increase in compressivestrength and thickening time that occurs in cement samples that have been addedquartz additive when compared with cement base.The result is made additive quartz sand as one alternative additive that canbe considered in terms of an increase in strength cement gas drilling in well withthe condition temperature and pressure high .The test results made in water content44 % and 50 % testing additive to value compressive strength very effectively inwater content 44 % with a temperature 27 ºC and 80 ºC the test results obtained of2161 psi and 5087 psi. While in water 50 % a decline in compressive strength andthickening time, by concentration of the additive 7 % of the highest compressivestrength of 4148 psi at the temperature 80 ºC.