Studi Laboratorium Pengaruh Penggunaan Pasir Kuarsa Sbg Aditif Terhadap Sifat Fisik Semen Kelas G Sesuai Standar Api 10a


Oleh : Adharta Astantio

Info Katalog

Nomor Panggil : 987/TP/2018

Penerbit : FTKE - Usakti

Kota Terbit : Jakarta

Tahun Terbit : 2018

Pembimbing 1 : Lilik Zabidi

Pembimbing 2 : Ridha Husla

Subyek : Cementing - Well construction;The function of drilling cement;Water cement ratio

Kata Kunci : well construction, cementing, compressive


File Repositori
No. Nama File Ukuran (KB) Status
1. 2018_TA_TM_07111002_Halaman-Judul.pdf 2875.26
2. 2018_TA_TM_07111002_Bab-1.pdf 632.72
3. 2018_TA_TM_07111002_Bab-2.pdf 1455.35
4. 2018_TA_TM_07111002_Bab-3.pdf 1537.58
5. 2018_TA_TM_07111002_Bab-4.pdf 1413.19
6. 2018_TA_TM_07111002_Bab-5.pdf 562.48
7. 2018_TA_TM_07111002_Dadftar-pustaka.pdf 554.42
8. 2018_TA_TM_07111002_Lampiran.pdf 1433.07

S Salah satu faktor yang mempengaruhi kualitas konstruksi sumur adalahsejauh mana kualitas semen yang dapat digunakan. Agar hasil penyemenan sesuaidengan yang diinginkan, sifat–sifat bubur semen harus sesuai dengan kondisiformasi. Kualitas bubur semen yang akan digunakan dalam proses penyemenandapat dilihat dari beberapa parameter kualitas semen, meliputi nilai compressivestrength yang cukup besar dan thickening time yang sesuai target penyemenan.Tujuan penulis dalampenelitian ini adalah untuk mengetahui seberapa besarpeningkatan compressive strength dan thickening time yang terjadi pada sampelsemen yang telah ditambahkan additive Pasir Kuarsa bila dibandingkan dengansemen dasar.Hasilnya adalah additive Pasir Kuarsa sebagai salah satu alternatif additiveyang dapat dipertimbangkan dalam hal peningkatan strength semen pemboran padasumur dengan kondisi temperatur dan tekanan yang tinggi. Hasil test yang didapatdengan tempratur 80ºC dan waktu perendaman 16 jam menghasilkan compressivestrength sangat efektif pada konsentrasi 10 % dengan hasil test 4.520 psi,temperatur 80ºF dan waktu perendaman 24 jam dengan hasil test 4.650 psi dengankonsentrasi 8 %, Lalu pengujian pada additive Pasir kuarsa dengan temperatur 100ºF dan waktu perendaman 16 jam menghasilkan compressive strength sangatefektif pada konsentrasi 10 % dengan hasil test 4.940 psi, temperatur 100ºF danwaktu perendaman 24 jam dengan hasil test 4.720 psi dengan konsentrasi 6 %.

O One of the factor that affect the quality of well construction is the quality ofcement used. In order for the cementing accordance with the desired, properties ofcement slurry must compatible with the condition of formation. The quality ofcement slurry to be used in process of cementing could be observed from severalparameter, include the large value of compressive strength and thickening timebased on target cementing.The purpose of this study is to find how much increase in compressivestrength and thickening time that occurs in cement samples that have been addedquartz additive when compared with cement base.The result is to add Quartz Sand Additive as an alternative additive that canbe considered in terms of increasing strength of drilling cement at wells with hightemperature and pressure conditions. The test result obtained with 80ºF tempratureand 16 hours of immersion time produces very effective compressive strength atconcentration of 10% with 4.520 psi test result, 80ºF temperature and immersion time 24 hours with 4.650 psi test result with 8% concentration, then test on quartzsand additive with a temperature of 100ºF and 16 hours of immersion time producesvery effective compressive strength at concentration of 10% with 4.940 psi testresult, 100ºF temperature and 24 hours immersion time with 4.720 psi test with 6%concentration..